cold rolled steel – What Is Piping

As per the World Steel Association there are over 3,500 different steel grades with unique properties are available. The manufacturing processes of steel contributes significantly towards the properties of final product. Hot rolling and cold rolling are two such processing of steel that affects the overall performance and application. In this article, we will discuss, the main differences between hot rolled and cold rolled steel. What is Hot Rolled Steel? Hot rolled steel is produced by rolling the steel at a temperatures above the steel’s recrystallization temperature (>1700° F.). Heating the steel above the recrystallization temperature makes steel easier to shape and form, and the steel can be produced in much larger sizes. For products where tight tolerances are not required, Hot rolled steel is ideal. The manufacturing of hot rolled steel starts with heating a large billet. Next, it is sent for pre-processing and the billet turns into a large roll. The final dimension is achieved by running it through a series of rollers at high temperature. For sheet metal, hot rolled steel is spun into coils and left to cool. For other forms like bars or plates, materials are sectioned and packaged for despatch. What is Cold Rolled Steel? Cold rolled steel is produced in cold reduction mills by processing the hot rolled steel after cooling it to room temperature. Cold rolled steels can be produced with tighter dimensional tolerances and a wide range of surface finishes. Differences between Hot Rolled and Cold Rolled Steel Let's find out the main differences between hot rolled and cold rolled steel. Differences between hot rolled and cold rolled steel Hot Rolled vs Cold Rolled Steel: Mechanical Properties Cold-rolled steel members normally has around 20% increase in mechanical strength because of strain hardening. The hardness value also increases while making cold rolled steel from hot rolled steel due to cold forming. So cold rolled steel members are stronger and harder than hot rolled steel members. As the metal is shaped at the lower temperatures, due to work hardening effect, the cold rolled steel’s hardness, resistance against tension breaking and deformation are all increased. Depending on the grades of the steel the mechanical properties vary. In the following table, a comparison of common mechanical properties for hot rolled and cold rolled steel grade 1018 is provided to get a feel of the mechanical property changes. Mechanical PropertiesHot RolledCold Rolled% changeTensile Strength67,000 psi85,000 psi26.9Yield Strength45,000 psi70,000 psi55.6Reduction of Area5855-5.2Elongation in 2"3628-22.2Brinell Hardness13716718.0Table 1: Hot Rolled vs cold Rolled Steel - Mechanical Properties Hot Rolled vs Cold Rolled Steel: Manufacturing, Cost Hot rolled steel manufacturing is done above recrystallization temperature whereas cold rolled steel involves much lower temperatures, generally room temperature. As the metal is hot in hot rolled steel, it needs less force and energy to shape it. But the force and energy requirement to shape a cold rolled product is more. Hot rolled steel is easier to make. Cold rolled steel involves further processing steps that increases the manufacturing steps as well as time requirement. So, overall the cost of cold rolled steel is much higher than hot rolled steel of same grade. Hot Rolled vs Cold Rolled Steel: Surface characteristics Hot rolled steel is characterised by a scaly surface, slightly rounded corners and edges and the surface is not smooth and non-oily. On the contrary, cold rolled steel comes with an oily or greasy finish, very smooth surface, and very sharp edges. The concentricity, and straightness of cold rolled steel is better when compared to hot rolled. Hot Rolled vs Cold Rolled Steel: Dimensional Tolerances Cold rolled steel can produce tighter tolerances for products as compared to hot rolled steel. More consistent and accurate shape is the feature of cold rolled steel. For bars, they produce true and square sections. Pipes and tubes of uniform concentricity and straightness are produces using cold rolled steel. On the other hand, due to shrinkage during cooling dimensional imperfections exist in hot rolled steel. Hot Rolled vs Cold Rolled Steel: Applications Most popular commercially available shapes are made from hot rolled steel. All structural members like UC, UB, RSA, PFC, etc and blooms, billets, sheets, slabs, tubes, bars, etc are hot rolled. On the contrary, only fewer specific shapes like Sheets, box section shapes (CHS, SHS, RHS), and round shapes are made from cold rolled steel. Hot rolled steels are widely used as structural beams, railroad tracks, sheet metal, automotive frames, agricultural equipment, etc. Cold rolled steel find their application as bars, rods, strips, pipes, metal furniture, aerospace structure, hole appliances, roof and wall systems. Hot Rolled vs Cold Rolled Steel: Disadvantages Poor surface finish, lower hardness and strength is the only concern for hot rolled steel. Cold work treatments in cold rolled steel can create internal stresses and unpredictable warping.